Tumbaga is the name given by Spanish Conquistadors for a non-specific alloy of gold and copper, and metals composed of these elements. Pieces made of tumbaga were widely found in pre-Columbian Mesoamerica in North America and South America.
![](http://upload.wikimedia.org/wikipedia/commons/thumb/6/6a/Tumbaga_Pectoral%2C_Quimbaya_culture.jpg/250px-Tumbaga_Pectoral%2C_Quimbaya_culture.jpg)
The term is a borrowing from the Tagalog tumbaga. This came from Malay tembaga, meaning 'copper' or 'brass'.[1] It has also been spelled tumbago in literature.[2]
Composition and properties
editTumbaga is an alloy composed mostly of gold and copper. It has a significantly lower melting point than gold or copper alone [citation needed]. It is harder than copper, but maintains malleability after being pounded.
Tumbaga can be treated with a carboxylic acid, such as oxalic acid, to dissolve copper off the surface. What remains is a shiny layer of nearly pure gold on top of a harder, more durable copper-gold alloy sheet. This process is referred to as depletion gilding.
Use and function
editTumbaga was widely used by the pre-Columbian cultures of Central and South America to make religious objects, as they considered gold a sacred metal. Like most gold alloys, tumbaga was versatile and could be cast, drawn, hammered, gilded, soldered, welded, plated, hardened, annealed, polished, engraved, embossed, and inlaid.
The proportion of gold to copper in artifacts varies widely; some items have been found with as much as 97% gold while others contain 97% copper. Some tumbaga has also been found to be composed of metals besides gold and copper, up to 18% of the total mass of the tumbaga.[citation needed]
Tumbaga objects were often made using a combination of the lost wax technique and depletion gilding. An alloy of varying proportions of copper, silver, and gold (typically in a percentage ratio of 80:15:5) was cast. It was burned after removal, turning surface copper into copper oxide, which was mechanically removed.[clarification needed] The object was placed in an oxidizing solution, likely composed of sodium chloride (salt) and ferric sulfate. This dissolved the silver from the surface, leaving only gold. When viewed through a microscope, voids appear where the copper and silver had been.
The "Tumbaga" Wreck
editIn 1992, approximately 200 silver "tumbaga" bars were recovered in wreckage off Grand Bahama Island. They were composed mainly of silver, copper, and gold plundered by the Spaniards during the conquests of Cortés and hastily melted into bars of tumbaga for transport across the Atlantic. Such bars were typically melted back into their constituent metals in Spain.[3]
See also
edit- Guanín – Pre-Columbian central American alloy
- Tombac – Copper-zinc alloy
- Orichalcum – Fabulous metal mentioned in ancient writings, such as the story of Atlantis in the Critias of Plato
References
edit- ^ "tumbaga", Wiktionary, 2022-07-27, retrieved 2023-01-06
- ^ Fester, G. A. (1962). "Copper and Copper Alloys in Ancient Argentina". Chymia. 8: 21–31. doi:10.2307/27757215. JSTOR 27757215.
- ^ The "Tumbaga" Saga: Treasure of the Conquistadors. Daniel Frank Sedwick. 2010. ISBN 978-0982081822.
External links
edit- Shipwreck recovered right after the conquest of Cortés with tumbaga gold bars
- The "Tumbaga" Saga: Treasure of the Conquistadors. Book about Tumbaga Bars
- The Art of Precolumbian Gold: The Jan Mitchell Collection, an exhibition catalog from The Metropolitan Museum of Art (fully available online as PDF), which contains material on Tumbaga