Eutectic system

(Redirected from Eutectic salt)

A eutectic system or eutectic mixture (/jˈtɛktɪk/ yoo-TEK-tik)[1] is a type of a homogeneous mixture that has a melting point lower than those of the constituents.[2] The lowest possible melting point over all of the mixing ratios of the constituents is called the eutectic temperature. On a phase diagram, the eutectic temperature is seen as the eutectic point (see plot on the right).[3]

A phase diagram for a fictitious binary chemical mixture (with the two components denoted by A and B) used to depict the eutectic composition, temperature, and point. (L denotes the liquid state.)

Non-eutectic mixture ratios have different melting temperatures for their different constituents, since one component's lattice will melt at a lower temperature than the other's. Conversely, as a non-eutectic mixture cools down, each of its components solidifies into a lattice at a different temperature, until the entire mass is solid.

Not all binary alloys have eutectic points, since the valence electrons of the component species are not always compatible[clarification needed] in any mixing ratio to form a new type of joint crystal lattice. For example, in the silver-gold system the melt temperature (liquidus) and freeze temperature (solidus) "meet at the pure element endpoints of the atomic ratio axis while slightly separating in the mixture region of this axis".[4]

In the real world, eutectic properties can be used to advantage in such processes as eutectic bonding, where silicon chips are bonded to gold-plated substrates with ultrasound, and eutectic alloys prove valuable in such diverse applications as soldering, brazing, metal casting, electrical protection, fire sprinkler systems, and nontoxic mercury substitutes.

The term eutectic was coined in 1884 by British physicist and chemist Frederick Guthrie (1833–1886). The word originates from Greek εὐ- (eû) 'well' and τῆξῐς (têxis) 'melting'.[2] Before his studies, chemists assumed "that the alloy of minimum fusing point must have its constituents in some simple atomic proportions", which was indeed proven to be not the case.[5]

Eutectic phase transition

edit
 
Four eutectic structures: A) lamellar B) rod-like C) globular D) acicular.

The eutectic solidification is defined as follows:[6]

 

This type of reaction is an invariant reaction, because it is in thermal equilibrium; another way to define this is the change in Gibbs free energy equals zero. Tangibly, this means the liquid and two solid solutions all coexist at the same time and are in chemical equilibrium. There is also a thermal arrest for the duration of the phase change during which the temperature of the system does not change.[6]

The resulting solid macrostructure from a eutectic reaction depends on a few factors, with the most important factor being how the two solid solutions nucleate and grow. The most common structure is a lamellar structure, but other possible structures include rodlike, globular, and acicular.[7]

Non-eutectic compositions

edit

Compositions of eutectic systems that are not at the eutectic point can be classified as hypoeutectic or hypereutectic:

  • Hypoeutectic compositions are those with a greater composition of species α and a smaller percent composition of species β than the eutectic composition (E)
  • Hypereutectic compositions are characterized as those with a higher composition of species β and a lower composition of species α than the eutectic composition.

As the temperature of a non-eutectic composition is lowered the liquid mixture will precipitate one component of the mixture before the other. In a hypereutectic solution, there will be a proeutectoid phase of species β whereas a hypoeutectic solution will have a proeutectic α phase.[6]

Types

edit

Alloys

edit

Eutectic alloys have two or more materials and have a eutectic composition. When a non-eutectic alloy solidifies, its components solidify at different temperatures, exhibiting a plastic melting range. Conversely, when a well-mixed, eutectic alloy melts, it does so at a single, sharp temperature. The various phase transformations that occur during the solidification of a particular alloy composition can be understood by drawing a vertical line from the liquid phase to the solid phase on the phase diagram for that alloy.

Some uses for eutectic alloys include:

Others

edit
 
Solid–liquid phase change of ethanol–water mixtures
  • Sodium chloride and water form a eutectic mixture whose eutectic point is −21.2 °C[9] and 23.3% salt by mass.[10] The eutectic nature of salt and water is exploited when salt is spread on roads to aid snow removal, or mixed with ice to produce low temperatures (for example, in traditional ice cream making).
  • Ethanol–water has an unusually biased eutectic point, i.e. it is close to pure ethanol, which sets the maximum proof obtainable by fractional freezing.
  • "Solar salt", 60% NaNO3 and 40% KNO3, forms a eutectic molten salt mixture which is used for thermal energy storage in concentrated solar power plants.[11] To reduce the eutectic melting point in the solar molten salts, calcium nitrate is used in the following proportion: 42% Ca(NO3)2, 43% KNO3, and 15% NaNO3.
  • Lidocaine and prilocaine—both are solids at room temperature—form a eutectic that is an oil with a 16 °C (61 °F) melting point that is used in eutectic mixture of local anesthetic (EMLA) preparations.
  • Menthol and camphor, both solids at room temperature, form a eutectic that is a liquid at room temperature in the following proportions: 8:2, 7:3, 6:4, and 5:5. Both substances are common ingredients in pharmacy extemporaneous preparations.[12]
  • Minerals may form eutectic mixtures in igneous rocks, giving rise to characteristic intergrowth textures exhibited, for example, by granophyre.[13]
  • Some inks are eutectic mixtures, allowing inkjet printers to operate at lower temperatures.[14]
  • Choline chloride produces eutectic mixtures with many natural products such as citric acid, malic acid and sugars. These liquid mixtures can be used, for example, to obtain antioxidant and antidiabetic extracts from natural products.[15]

Strengthening mechanisms

edit

Alloys

edit

The primary strengthening mechanism of the eutectic structure in metals is composite strengthening (See strengthening mechanisms of materials). This deformation mechanism works through load transfer between the two constituent phases where the more compliant phase transfers stress to the stiffer phase.[16] By taking advantage of the strength of the stiff phase and the ductility of the compliant phase, the overall toughness of the material increases. As the composition is varied to either hypoeutectic or hypereutectic formations, the load transfer mechanism becomes more complex as there is a load transfer between the eutectic phase and the secondary phase as well as the load transfer within the eutectic phase itself.

A second tunable strengthening mechanism of eutectic structures is the spacing of the secondary phase. By changing the spacing of the secondary phase, the fraction of contact between the two phases through shared phase boundaries is also changed. By decreasing the spacing of the eutectic phase, creating a fine eutectic structure, more surface area is shared between the two constituent phases resulting in more effective load transfer.[17] On the micro-scale, the additional boundary area acts as a barrier to dislocations further strengthening the material. As a result of this strengthening mechanism, coarse eutectic structures tend to be less stiff but more ductile while fine eutectic structures are stiffer but more brittle.[17] The spacing of the eutectic phase can be controlled during processing as it is directly related to the cooling rate during solidification of the eutectic structure. For example, for a simple lamellar eutectic structure, the minimal lamellae spacing  is:[18]

 

Where  is   is the surface energy of the two-phase boundary,   is the molar volume of the eutectic phase,    is the solidification temperature of the eutectic phase,   is the enthalpy of formation of the eutectic phase, and   is the undercooling of the material. So, by altering the undercooling, and by extension the cooling rate, the minimal achievable spacing of the secondary phase is controlled.

Strengthening metallic eutectic phases to resist deformation at high temperatures (see creep deformation) is more convoluted as the primary deformation mechanism changes depending on the level of stress applied. At high temperatures where deformation is dominated by dislocation movement, the strengthening from load transfer and secondary phase spacing remain as they continue to resist dislocation motion. At lower strains where Nabarro-Herring creep is dominant, the shape and size of the eutectic phase structure plays a significant role in material deformation as it affects the available boundary area for vacancy diffusion to occur.[19]

Other critical points

edit
 
Iron–carbon phase diagram, showing the eutectoid transformation between austenite (γ) and pearlite.

Eutectoid

edit

When the solution above the transformation point is solid, rather than liquid, an analogous eutectoid transformation can occur. For instance, in the iron-carbon system, the austenite phase can undergo a eutectoid transformation to produce ferrite and cementite, often in lamellar structures such as pearlite and bainite. This eutectoid point occurs at 723 °C (1,333 °F) and 0.76 wt% carbon.[20]

Peritectoid

edit

A peritectoid transformation is a type of isothermal reversible reaction that has two solid phases reacting with each other upon cooling of a binary, ternary, ..., n-ary alloy to create a completely different and single solid phase.[21] The reaction plays a key role in the order and decomposition of quasicrystalline phases in several alloy types.[22] A similar structural transition is also predicted for rotating columnar crystals.

Peritectic

edit
 
Gold–aluminium phase diagram

Peritectic transformations are also similar to eutectic reactions. Here, a liquid and solid phase of fixed proportions react at a fixed temperature to yield a single solid phase. Since the solid product forms at the interface between the two reactants, it can form a diffusion barrier and generally causes such reactions to proceed much more slowly than eutectic or eutectoid transformations. Because of this, when a peritectic composition solidifies it does not show the lamellar structure that is found with eutectic solidification.

Such a transformation exists in the iron-carbon system, as seen near the upper-left corner of the figure. It resembles an inverted eutectic, with the δ phase combining with the liquid to produce pure austenite at 1,495 °C (2,723 °F) and 0.17% carbon.

At the peritectic decomposition temperature the compound, rather than melting, decomposes into another solid compound and a liquid. The proportion of each is determined by the lever rule. In the Al-Au phase diagram, for example, it can be seen that only two of the phases melt congruently, AuAl2 and Au2Al, while the rest peritectically decompose.

"Bad solid solution"

edit

Not all minimum melting point systems are "eutectic". The alternative of "poor solid solution" can be illustrated by comparing the common precious metal systems Cu-Ag and Cu-Au. Cu-Ag, source for example https://himikatus.ru/art/phase-diagr1/Ag-Cu.php, is a true eutectic system. The eutectic melting point is at 780 C, with solid solubility limits at fineness 80 and 912 by weight, and eutectic at 719. Since Cu-Ag is a true eutectic, any silver with fineness anywhere between 80 and 912 will reach solidus line, and therefore melt at least partly, at exactly 780 C. The eutectic alloy with fineness exactly 719 will reach liquidus line, and therefore melt entirely, at that exact temperature without any further rise of temperature till all of the alloy has melted. Any silver with fineness between 80 and 912 but not exactly 719 will also reach the solidus line at exactly 780 C, but will melt partly. It will leave a solid residue with fineness of either exactly 912 or exactly 80, but never some of both. It will melt at constant temperature without further rise of temperature until the exact amount of eutectic (fineness 719) alloy has melted off to divide the alloy into eutectic melt and solid solution residue. On further heating, the solid solution residue dissolves in the melt and changes its composition until the liquidus line is reached and the whole residue has dissolved away. Cu-Au source for example https://himikatus.ru/art/phase-diagr1/Au-Cu.php does display a melting point minimum at 910 C and given as 44 atom % Cu, which converts to about 20 weight percent Cu - about 800 fineness of gold. But this is not a true eutectic. 800 fine gold melts at 910 C, to a melt of exact same composition, and the whole alloy will melt at exact same temperature. But the differences happen away from the minimum composition. Unlike silver with fineness other than 719 (which melts partly at exactly 780 C through a wide fineness range), gold with fineness other than 800 will reach solidus and start partial melting at a temperature different from and higher than 910 C, depending on the alloy fineness. The partial melting does cause some composition changes - the liquid will be closer in fineness towards 800 than the remaining solid, but the liquid will not have fineness of exactly 800 and the fineness of the remaining solid will depend on the fineness of the liquid. The underlying reason is that for an eutectic system like Cu-Ag, the solubility in liquid phase is good but solubility in solid phase is limited. Therefore when a silver-copper alloy is frozen, it actually separates into crystals of 912 fineness silver and 80 fineness silver - both are saturated and always have the same composition at the freezing point of 780 C. Thus the alloy just below 780 C consists of two types of crystals of exactly the same composition regardless of the total alloy composition, only the relative amount of each type of crystals differs. Therefore they always melt at 780 C until one or other type of crystals, or both, will be exhausted. In contrast, in Cu-Au system the components are miscible at the melting point in all compositions even in solid. There can be crystals of any composition, which will melt at different temperatures depending on composition. However, Cu-Au system is a "poor" solid solution. There is a substantial misfit between the atoms in solid which, however, near the melting point is overcome by entropy of thermal motion mixing the atoms. That misfit, however, disfavours the Cu-Au solution relative to phases in which the atoms are better fitted, such as the melt, and causes the melting point to fall below the melting point of components.

Eutectic calculation

edit

The composition and temperature of a eutectic can be calculated from enthalpy and entropy of fusion of each components.[23]

The Gibbs free energy G depends on its own differential:

 

Thus, the G/T derivative at constant pressure is calculated by the following equation:

 

The chemical potential   is calculated if we assume that the activity is equal to the concentration:

 

At the equilibrium,  , thus   is obtained as

 

Using[clarification needed] and integrating gives

 

The integration constant K may be determined for a pure component with a melting temperature   and an enthalpy of fusion  :

 

We obtain a relation that determines the molar fraction as a function of the temperature for each component:

 

The mixture of n components is described by the system

 
 

which can be solved by

 

See also

edit

References

edit
  1. ^ "eutectic". Merriam-Webster.com Dictionary. Merriam-Webster.
  2. ^ a b Guthrie, Frederick (June 1884). "LII. On eutexia". The London, Edinburgh, and Dublin Philosophical Magazine and Journal of Science. 5th series. 17 (108): 462–482. doi:10.1080/14786448408627543. p. 462: The main argument of the present communication hinges upon the existence of compound bodies, whose chief characteristic is the lowness of their temperatures of fusion. This property of the bodies may be called Eutexia, the bodies possessing it eutectic bodies or eutectics (εὖ τήκειν).
  3. ^ Smith & Hashemi 2006, pp. 326–327
  4. ^ "Collection of Phase Diagrams". www.crct.polymtl.ca.
  5. ^ Britain), Chemical Society (Great (1885). Journal of the Chemical Society. Chemical Society.
  6. ^ a b c Smith & Hashemi 2006, p. 327.
  7. ^ Smith & Hashemi 2006, pp. 332–333.
  8. ^ "Operation of the Overloads". Retrieved 2015-08-05.
  9. ^ Muldrew, Ken; Locksley E. McGann (1997). "Phase Diagrams". Cryobiology—A Short Course. University of Calgary. Archived from the original on 2006-06-15. Retrieved 2006-04-29.
  10. ^ Senese, Fred (1999). "Does salt water expand as much as fresh water does when it freezes?". Solutions: Frequently asked questions. Department of Chemistry, Frostburg State University. Retrieved 2006-04-29.
  11. ^ "Molten salts properties". Archimede Solar Plant Specs. Archived from the original on 2020-04-20. Retrieved 2011-07-15.
  12. ^ Phaechamud, Thawatchai; Tuntarawongsa, Sarun; Charoensuksai, Purin (October 2016). "Evaporation Behavior and Characterization of Eutectic Solvent and Ibuprofen Eutectic Solution". AAPS PharmSciTech. 17 (5): 1213–1220. doi:10.1208/s12249-015-0459-x. ISSN 1530-9932. PMID 26669887.
  13. ^ Fichter, Lynn S. (2000). "Igneous Phase Diagrams". Igneous Rocks. James Madison University. Archived from the original on 2011-06-28. Retrieved 2006-04-29.
  14. ^ US 5298062A, Davies, Nicholas A. & Nicholas, Beatrice M., "Eutectic compositions for hot melt jet inks", published 1994-03-29, issued 1994-03-29 
  15. ^ Socas-Rodriguez, Bárbara; Torres-Cornejo, Mónica Vanesa; Álvarez-Rivera, Gerardo; Mendiola, Jose A. (May 2021). "Deep Eutectic Solvents for the Extraction of Bioactive Compounds from Natural Sources and Agricultural By-Products". Applied Sciences. 11 (1): 4897. doi:10.3390/app11114897. hdl:10261/253199. ISSN 2076-3417.
  16. ^ Courtney, T. H. (1990). Mechanical behavior of materials (2nd ed.). New York: McGraw-Hill.
  17. ^ a b Callister, W. D. (2010). Materials science and engineering : an introduction.
  18. ^ Porter, D. A.; Easterling, K. E.; Sherif, M. Y. (2009). Phase transformations in metals and alloys.
  19. ^ Wu, T.; Plotkowski, A.; Shyam, A.; Dunand, D.C. "Microstructure and creep properties of cast near-eutectic Al-Ce-Ni alloys". Mater. Sci. Eng. A. 833: 12.
  20. ^ Ballentine, Kim (28 April 1996). "Iron-Iron Carbide Phase Diagram Example". Archived from the original (PDF) on 16 February 2008.
  21. ^ IUPAC, Compendium of Chemical Terminology, 2nd ed. (the "Gold Book") (1997). Online corrected version: (2006–) "Peritectoid reaction". doi:10.1351/goldbook.P04501
  22. ^ Das, Amit; Manna, Indranil; Pabi, S. K. (October 1999). "A numerical model of peritectoid transformation". Metallurgical and Materials Transactions A. 30 (10). The Minerals, Metals & Materials Society, ASM International: 2563–2573. Bibcode:1999MMTA...30.2563D. doi:10.1007/s11661-999-0295-2. S2CID 95279944.
  23. ^ Brunet, Luc E.; Caillard, Jean; André, Pascal (June 2004). "Thermodynamic Calculation of n-component Eutectic Mixtures". International Journal of Modern Physics C. 15 (5). World Scientific: 675–687. Bibcode:2004IJMPC..15..675B. doi:10.1142/S0129183104006121.

Bibliography

edit
  • Smith, William F.; Hashemi, Javad (2006), Foundations of Materials Science and Engineering (4th ed.), McGraw-Hill, ISBN 978-0-07-295358-9.

Further reading

edit